Suzhou Polywell Engineering Plastics Co.,Ltd
We provide overall solutions of PA thermal break strips. Including the PA66GF25 granules, the extruder, the mold, the thermal break strips and the broken bridge aluminum frames.
Add to Cart
Polyamide Fiberglass Reinforced Nylon PA66GF25 High Quality Raw Material
Nylon/PA66 granules reinforced by fiberglass with granulation capacity of 8,000 tons per year. The performance of final products of this raw material meet the national standard.
The product is based on PA66 resin, added with glass fiber, high-efficiency flame retardant and various additives, and extruded and blended by twin-screw extruder.
| Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| Melting point | ºC | ≥240 | ≥240 |
| Testing for tensile cracks | - | No cracks | No cracks |
| Shore hardness | - | 80±5 | 80-85 |
| Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| Elasticity modulus | MPa | ≥4500 | ≥4550 |
| Elongation at break | % | ≥2.5 | ≥2.6 |
| Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3. The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.4%~0.8%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
The PA66 granules with fiber glass are mainly used in thermal break strips, which are used in aluminum windows and doors. Our granules have good fluidity thus guaranteeing your smooth production. The good raw material can reduce the rate of rejects, and can produce high quality stips.
Packaging details:25kg/bag
Delivery details: shipped in 5-8 working days after receiving the payment
Before sales
1. introduce products in detail
2. recommend suitable solutions
3. provide with reference information
During manufacturing
1. provide with layout and engineering conditions
2. inform the processing status
3. offer related documents
After Sales
1. provide installation, commissioning and training
2. offer spare parts
3. Provide with necessary technical support